供应LCP美国杜邦7130L ，6130，6130L塑胶原料，注塑数据
②原料技术数据 | |||||
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 比重 | 黑色 | ASTM D-792 | 1.62 | --- |
泰伯摩擦 | --- | ASTM D-1044 | 63 | mg | |
模缩率 | 流向1.6mm | ASTM D-955 | -0.1 | % | |
模缩率 | 流向3.2mm | ASTM D-955 | 0 | % | |
模缩率 | 横向1.6mm | ASTM D-955 | 0.9 | % | |
机械性能 | 模缩率 | 横向3.2mm | ASTM D-955 | 0.8 | % |
洛氏硬度 | Scale M | ASTM D-785 | 63 | --- | |
冲击下机械性能 | --- | UL 746B | 210 | oC | |
拉伸强度 | 23℃,1.6mm | ASTM D-638 | 173 | MPa | |
拉伸强度 | 23℃,3.2mm | ASTM D-638 | 150 | MPa | |
断裂伸长率 | 23℃,1.6mm | ASTM D-638 | 1.6 | % | |
断裂伸长率 | 23℃,3.2mm | ASTM D-638 | 1.7 | % | |
拉伸模量 | 23℃,1.6mm | ASTM D-638 | 19306 | MPa | |
拉伸模量 | 23℃,3.2mm | ASTM D-638 | 18000 | MPa | |
弯曲模量 | 23℃,0.8mm | ASTM D-790 | 18000 | MPa | |
弯曲模量 | 23℃,1.6mm | ASTM D-790 | 14000 | MPa | |
弯曲模量 | 23℃,3.2mm | ASTM D-790 | 13100 | MPa | |
无缺口冲击强度 | 23℃,1.6mm | ASTM D-4812 | 840 | j/m | |
无缺口冲击强度 | 23℃,3.2mm | ASTM D-4812 | 555,20%NB | j/m | |
弯曲强度 | 23℃,0.8mm | ASTM D-790 | 215 | MPa | |
弯曲强度 | 23℃,1.6mm | ASTM D-790 | 192 | MPa | |
弯曲强度 | 23℃,3.2mm | ASTM D-790 | 183 | MPa | |
压缩强度 | 3.2mm | ASTM D-695 | 89 | MPa | |
弯曲疲劳 | 3.2mm，69MPa | ASTM D-671 | 2667 | cycle | |
IZOD冲击强度 | 23℃,0.8mm | ASTM D-256 | 400,40%NB | j/m | |
IZOD冲击强度 | 23℃,1.6mm | ASTM D-256 | 170 | j/m | |
IZOD冲击强度 | 23℃,3.2mm | ASTM D-256 | 225 | j/m | |
电气性能 | 介电强度 | 1.6mm逐步 | ASTM D-149 | 31 | KV/mm |
介电强度 | 23℃,1.6mm短时间 | ASTM D-149 | 35 | KV/mm | |
介电强度 | 23℃,3.2mm短时间 | ASTM D-149 | ＞28 | KV/mm | |
表面电阻率 | --- | ASTM D-257 | 1×1015 | Ω | |
体积电阻率 | --- | ASTM D-257 | 1×1016 | Ω.cm | |
损耗因素 | 23℃,3.2mm,1×109Hz | ASTM D-2520B | 0.004 | --- | |
损耗因素 | 23℃,0.8mm,1×109Hz | ASTM D-2520B | 0.004 | --- | |
损耗因素 | 23℃,1.6mm,1×109Hz | ASTM D-2520B | 0.004 | --- | |
损耗因素 | 23℃,0.8mm,1×103Hz | ASTM D-150 | 0.013 | --- | |
损耗因素 | 23℃,3.2mm,1×103Hz | ASTM D-150 | 0.013 | --- | |
损耗因素 | 23℃,0.8mm,1×106Hz | ASTM D-150 | 0.029 | --- | |
损耗因素 | 23℃,3.2mm,1×106Hz | ASTM D-150 | 0.029 | --- | |
介电常数 | 23℃,0.8mm,1×103Hz | ASTM D-150 | 3.9 | --- | |
介电常数 | 23℃,3.2mm,1×103Hz | ASTM D-150 | 4.3 | --- | |
介电常数 | 23℃,0.8mm,1×106Hz | ASTM D-150 | 3.5 | --- | |
介电常数 | 23℃,3.2mm,1×106Hz | ASTM D-150 | 3.8 | --- | |
介电常数 | 23℃,0.8mm,1×109Hz | ASTM D-2520B | 4.4 | --- | |
介电常数 | 23℃,3.2mm,1×109Hz | ASTM D-2520B | 4.3 | --- | |
加工性能 | 熔解温度范围 | ℃ | --- | 363～371 | --- |
模具温度范围 | ℃ | --- | 30～95 | --- | |
干燥时间（除湿干燥剂） | --- | --- | 2 | h | |
干燥温度 | --- | --- | 135 | ℃ | |
加工时水气含量 | --- | --- | ＜0.01 | % | |
热 性 能 | 相关温度指数 | --- | UL 746B | 240 | oC |
熔点 | --- | ASTM D-3418 | 352 | oC | |
导热性 | --- | ASTM C-177 | 0.32 | W/m k | |
热变形温度 | --- | ASTM D-648 | 289 | oC | |
玻璃转变温度 | --- | ASTM D-3418 | 120 | oC | |
外推*终融温 | --- | ASTM D-3418 | 360 | oC | |
其它性能 | 厚度测试 | --- | UL 94 | 0.75 | mm |